Characterization and Wear Behaviour of WC-Co Coated Copper under Dry Sliding Conditions at Varying Hardness
Pure copper was coated with Tungsten Carbide-Cobalt (WC12%-Co) using Detonation- Gun technique. A coating thickness of 541 µm was obtained and the hardness of WC-Co coated copper surface was 5.2 times greater than the hardness of uncoated surface. The wear properties of coated copper were investigat...