| Summary: | Magnetic properties of single crystalline Ga1−xFexTe (x = 0.05) have been measured. GaTe and related layered III-VI semiconductors exhibit a rich collection of important properties for THz generation and detection. The magnetization versus field for an x = 0.05 sample deviates from the linear response seen previously in Ga1−xMnxSe and Ga1−xMnxS and reaches a maximum of 0.68 emu/g at 2 K in 7 T. The magnetization of Ga1−xFexTe saturates rapidly even at room temperature where the magnetization reaches 50% of saturation in a field of only 0.2 T. In 0.1 T at temperatures between 50 and 400 K, the magnetization drops to a roughly constant 0.22 emu/g. In 0 T, the magnetization drops to zero with no hysteresis present. The data is consistent with Van-Vleck paramagnetism combined with a pronounced crystalline anisotropy, which is similar to that observed for Ga1−xFexSe. Neither the broad thermal hysteresis observed from 100-300 K in In1−xMnxSe nor the spin-glass behavior observed around 10.9 K in Ga1−xMnxS are observed in Ga1−xFexTe. Single crystal x-ray diffraction data yield a rhombohedral space group bearing hexagonal axes, namely R3c. The unit cell dimensions were a = 5.01 Å, b = 5.01 Å, and c = 17.02 Å, with α = 90°, β = 90°, and γ = 120° giving a unit cell volume of 369 Å3.
|
|---|