Improving the ductility of Mg-2.5Nd-0.5Zn-0.5Zr alloy by multi-pass hot rolling
Fine-grained, high-strength and high-ductility Mg-2.5Nd-0.5Zn-0.5Zr alloy sheets were prepared by multi-pass hot rolling with ultimate tensile strength of 311.9 MPa, yield strength of 272.4 MPa, elongation of 17.1%, and the average grain size of 4.25 μm. After multi-pass hot rolling, all plates show...