High-temperature defect recovery in self-ion irradiated W-5 wt% Ta
A study of high-temperature defect recovery has been carried out for W-5 wt% Ta alloy, irradiated with 2 MeV W+ ions at 500 °C, up to 1.2 dpa. After post-irradiation annealing at 1200 °C for 15 min, the damage microstructure evolved from a random distribution of small loops to a mixture of large loo...