Stress Corrosion Crack Nucleation in Alloy 600 and the Effect of Surface Modification
The stress corrosion cracking (SCC) condition for Alloy 600 was determined for various stress modes: constant-strain standard C-ring, and indentation, used to localize cracks for interrogation with x-ray techniques such as micro Laue diffraction (MLD). The SCC cracks nucleated on both the indentatio...