Hot workability of magnesium alloys
For the alloy AZ91 (Mg-9.OAl-0.7Zn-0.13Mn) die cast specimens were subjected to torsion testing at 150, 180, 240, 300, 420 and 450C̕ at 0.05 0.5 and 5.0 s -1 The as-cast specimens exhibited hot shortness at 360C̕ and above; however in that domain, after prior thermomechanical processing (TMP) at 300...
| Main Author: | |
|---|---|
| Format: | Others |
| Published: |
1997
|
| Online Access: | http://spectrum.library.concordia.ca/385/1/NQ39793.pdf Mwembela, Aaron Absalom <http://spectrum.library.concordia.ca/view/creators/Mwembela=3AAaron_Absalom=3A=3A.html> (1997) Hot workability of magnesium alloys. PhD thesis, Concordia University. |