Repair Welding and Microstructural Characterization of Nickel-Based IN738LC Gas Turbine Blades
碩士 === 長庚大學 === 機械工程研究所 === 87 === It was observed that an acicular phase formed in the matrix of IN738LC turbine blades, which were used at elevated temperatures for a prolonged period of time. As a result, cracking was a common problem encountered during repair welding of IN738LC blades. In this...