Investigation of microstructure and mechanical properties of hot-pressed Titanium Silicon Carbide
碩士 === 國立成功大學 === 材料科學及工程學系碩博士班 === 92 === Polycrystalline samples of Ti3SiC2 were prepared with different molar ratio of Ti / Si / C powders as starting materials, then hot-pressed at 1550℃ for 30minutes under mechanical pressure of 25MPa. Results show that sample made with 3Ti / 1.1Si / 2C molar...