Failure Mechanism of Electromigration for Flip-Chip SnAg3.5 Solder Joints
博士 === 國立交通大學 === 材料科學與工程系所 === 94 === Electromigration behavior of lead-free SnAg3.5 solder joints was investigated under the average current densities of 1 �e 104 A/cm2 and 5 �e 103 A/cm2 at 150℃. Different failure modes were observed for the above two stressing conditions. When stressed at 1 �e...
Main Authors: | Tung Liang Shao, 邵棟樑 |
---|---|
Other Authors: | Chih Chen |
Format: | Others |
Language: | en_US |
Published: |
2005
|
Online Access: | http://ndltd.ncl.edu.tw/handle/08288625847433983410 |
Similar Items
-
Electromigration Studies of SnAg3.5 Flip Chip Solder Bumps
by: Yi-Hsiung Chen, et al.
Published: (2003) -
Electromigration Study of Ni/SnAg/Ni Flip-Chip Solder Joints
by: Wu, Wei-Ming, et al.
Published: (2018) -
Electromigration tests in Cu/SnAg/Ni/Cu Flip Chip solder joints and Cu/SnAg/Cu microbumps
by: Liu, Shun Cai, et al.
Published: (2014) -
Effect of UBM structure on Electromigration and thermomigration behavior in flip chip SnAg solder joints
by: Yang, Zong_Lin, et al.
Published: (2011) -
Electromigration Study In Flip-Chip SnAg Solder Joints With 5μm Cu Under-Bump-Metallization
by: Shih, Yu Cho, et al.
Published: (2010)