Effects of Minor Scandium Additions on the Glass-Forming Ability and Mechanical Properties of Zr-Cu-Al-Ni Metallic Glass
碩士 === 國立臺北科技大學 === 材料科學與工程研究所 === 97 === The XRD pattern for (Zr50Cu35Ni6Al9)100-XScX(X=0,0.02,0.05, 0.1, 0.5, 1at.%) alloy ribbons and the rods (X=0.1, 0.5, 1at.%) with a diameter of 4mm consist of only broad diffraction maxima without any sharp Bragg peak, indicating that they are amorphous in st...