An Investigation of the Hardening Mechanism of Annealed Trivalent Chromium-Carbon Deposit
博士 === 長庚大學 === 機械工程學系 === 100 === Several researchers have pointed out that the hardness of a Cr-C deposit obtained from a trivalent Cr-based plating bath can be increased to 1600 Hv after annealing at 600 °C for 1 h. They believed that the precipitation of fine Cr-carbides is the main hardening me...