Oxidation behavior of high silicon content Ta–Si–N coatings in ambient air
碩士 === 國立臺灣海洋大學 === 材料工程研究所 === 105 === Ta–Si–N coatings were prepared using reactive direct current magnetron co-sputtering on silicon substrates. The sputter power was set at 100 W for each target, and the N2/(N2+Ar) was fixed at 0.1 to 0.4; the substrate holder rotated was set at 1 to 30 rpm. The...
Main Authors: | Gao, Yu-Xiang, 高裕翔 |
---|---|
Other Authors: | Chen, Yung-I |
Format: | Others |
Language: | zh-TW |
Published: |
2017
|
Online Access: | http://ndltd.ncl.edu.tw/handle/u8vbc4 |
Similar Items
-
Oxidation resistance and mechanical properties of Ta–Si–N coatings
by: Kun-Yi Lin, et al.
Published: (2013) -
Oxidation Behavior and Structural Transformation of (CrTaTiVZr)N Coatings
by: Zue-Chin Chang, et al.
Published: (2020-04-01) -
The Effect of Silicon Content on the High Temperature Oxidation Behavior of Si-containing Steel
by: Yu-Ling Yang, et al.
Published: (2006) -
Mechanical Properties and Oxidation Behavior of Cr–Si–N Coatings
by: Li-Chun Chang, et al.
Published: (2019-08-01) -
Oxidation Resistance and Mechanical Properties of CrTaSiN Coatings Prepared Using Co-sputter Deposition
by: Wang, Hsiu-Hui, et al.
Published: (2014)