Influence of an MgTiTaON inserted layer on magmetic properties and microstructure of FePtAgC films
碩士 === 國立中興大學 === 材料科學與工程學系所 === 107 === The FePt film above 10 nm critical lattice relaxation thickness was prepared and the ultrathin MgTiTaON layer was interleaved in between FePt film and the multilayer stack is FePt(6 nm)/[MgTiTaON(1 nm)/FePt(4 nm)]2. Next, the FePt films were co-sputtered with (A...