Formation of Inclusions and their Development during Secondary Steelmaking
Al–O relations in iron were investigated. Pure iron with varying Al content was equilibrated at 1873 K. The oxygen content of iron with higher Al content than 1.0 mass % was found to be much lower than previous works, while the oxygen content for Al content less than 1 mass% was found to be slightly...