Erosion during Brazing in Stainless Steel grade 304
The erosion or dissolution of stainless steel grade 304 as base metal by molten brazing fillermetal was investigated using one nickel and two iron based filler metals. The difference betweentwo iron filler metal is 5 % Manganese content in one of the filler metal. The Wettability of fillermetal is e...