The Susceptibility to Hydrogen Induced Stress Cracking for Alloy 718 and Alloy 725
The Hydrogen Induced Stress Cracking (HISC) susceptibility of Alloy 718 and Alloy 725 where examined and compared. Pre-charged samples of each alloy where stepwise loaded during polarization in Cortest Proof rings. A safe load was found from this stepwise loading. To confirm that these load levels w...