Effect of residual stress gradients in austenitic stainless steels on stress corrosion cracking
<p>The effect of the residual stresses developed during simulated weld heat affected zone in austenitic stainless steel specimen on the stress corrosion cracking susceptibility was studied. Residual stresses was measured using X-ray diffraction technique. Boiling Magnesium Chloride was used as...