Effect of processing induced defects on the failure characteristics of graphite epoxy angles
The objective of this study was to investigate the bending strength and failure characteristics of AS4/3501-6 and AS4/1806 graphite/epoxy angles sections as a function of processing induced defects and porosity. The angle sections were removed from 30-inch long angles fabricated at Lockheed Georgia...