Thermomechanical properties of polymers at high rates of strain
-1 were achieved when testing specimens and this rate was obtained using a split Hopkinson pressure bar. A substantial number of preliminary tests were conducted in order to obtain a suitable specimen size which was then used in the temperature measurement process. Quasistatic, intermediate and high...